DSpace Repository

Influencia del sistema de adhesivos universales con silano sobre los valores de resistencia de unión en cerámicas de disilicato de litio, maquinada e inyectada

Show simple item record

dc.contributor.advisor Domínguez, John Alexis es_ES
dc.contributor.advisor Espejo Loyola, Dalma Flor es_ES
dc.contributor.author Calderón Gonzales, Valeria Jackeline es_ES
dc.contributor.author Gomez Diaz, Wendy Alejandra es_ES
dc.date.accessioned 2022-01-18T21:01:26Z
dc.date.available 2022-01-18T21:01:26Z
dc.date.issued 2021
dc.identifier.other 104125 es_ES
dc.identifier.uri https://hdl.handle.net/20.500.12866/11223
dc.description.abstract Antecedentes: El creciente requerimiento de los pacientes por obtener restauraciones de alta resistencia, calidad y estética es una competencia clave para nosotros, las restauraciones cerámicas son las más conocidas y usadas, es importante comprender que la adhesión es un proceso imprescindible para el éxito. Objetivo: Determinar el efecto del sistema de adhesivos universales con silano sobre los valores de resistencia de unión al Disilicato de Litio maquinadas e inyectadas. Materiales y Métodos: El estudio fue experimental (in vitro), la muestra estuvo conformada por 20 discos de disilicato de litio de 10 mm, IPS e.max CAD (Ivoclar Vivadent, Liechtenstein, Suiza) 10 maquinadas y 10 inyectadas, que fueron colocadas en tubos de policloruro de vinilo (PVC). Los discos fueron encajados a la máquina de ensayo universal para la demostración del microcizallamiento y se anotaron los valores indicados en MPa. Se realizó un análisis descriptivo mediante la obtención de los promedios de resistencia de unión de cada uno de los grupos, luego se evaluó la normalidad de los datos mediante la prueba de D’Agostino, y la diferencia estadística se midió con la prueba PosTukey. Resultados: Grupo A1 obtuvo el valor de resistencia de unión de 08.86 ± 1.85 Mpa. Grupo A2 el valor de 08.39± 2.48 Mpa. Grupo B1, el valor de 12.34 ± 2.97Mpa. Grupo B2, el valor de 10.17± 2.18 Mpa. Conclusiones: Según los adhesivos evaluados en este estudio Ambar Universal APS presentó mayores resultados en los valores de resistencia de unión tanto en disilicato de litio maquinada e inyectada. es_ES
dc.description.abstract Background: The increasing requirement of patients to obtain restorations of high resistance, quality and aesthetics is a key competence for us, the ceramic restorations are the best known and most used, it is important to understand that adhesion is an essential process for the success. Objective: Determine the effect of the system of universal adhesives with silane on the values of resistance of union to the machined and injected Lithium Disilicate. Materials and Methods: The study was experimental (in vitro), the sample consisted of 20 lithium disilicate discs of 10 mm, IPS e.max CAD (Ivoclar Vivadent, Liechtenstein, Switzerland) 10 machined and 10 injected, which were placed in polyvinyl chloride (PVC) pipes. The disks were fitted to the universal testing machine for the demonstration of micro-shear and the indicated values in MPa were noted. A descriptive analysis was carried out by obtaining the averages of binding resistance of each of the groups, then the normality of the data was evaluated using the D'Agostino test, and the statistical difference was measured with Pos teste Tukey. Results: Group A1 obtained the average bond strength values of 08.86 ± 1.85 Mpa. Group A2 the value of 08.39 ± 2.48 MPa. Group B1, the value of 12.34 ± 2.97Mpa. Group B2, the value of 10.17 ± 2.18 Mpa. Conclusions: According to the adhesives evaluated in this study, Ambar Universal APS presented higher results in bond strength values in both machined and injected lithium disilicate. es_ES
dc.format application/pdf es_ES
dc.language.iso spa es_ES
dc.publisher Universidad Peruana Cayetano Heredia es_ES
dc.rights info:eu-repo/semantics/openAccess es_ES
dc.rights.uri https://creativecommons.org/licenses/by-nc-nd/4.0/deed.es es_ES
dc.subject Microcizallamiento es_ES
dc.subject Adhesivos es_ES
dc.subject Silano es_ES
dc.title Influencia del sistema de adhesivos universales con silano sobre los valores de resistencia de unión en cerámicas de disilicato de litio, maquinada e inyectada es_ES
dc.title.alternative Influence of the universal adhesives system with silane on the bonding strength values in lithium disilicate ceramics, machined and injected es_ES
dc.type info:eu-repo/semantics/bachelorThesis es_ES
thesis.degree.name Cirujano Dentista es_ES
thesis.degree.grantor Universidad Peruana Cayetano Heredia. Facultad de Estomatología Roberto Beltrán Neira es_ES
thesis.degree.discipline Estomatología es_ES
dc.publisher.country PE es_ES
dc.subject.ocde http://purl.org/pe-repo/ocde/ford#2.05.02 es_ES
dc.subject.ocde http://purl.org/pe-repo/ocde/ford#3.02.14 es_ES
renati.author.dni 71625145
renati.author.dni 74293745
renati.advisor.orcid https://orcid.org/0000-0002-8214-6171 es_ES
renati.advisor.orcid https://orcid.org/0000-0001-5134-0580 es_ES
renati.advisor.dni 49046157
renati.advisor.dni 72071589
renati.type http://purl.org/pe-repo/renati/type#tesis es_ES
renati.level http://purl.org/pe-repo/renati/nivel#tituloProfesional es_ES
renati.discipline 911016 es_ES
renati.juror Delgado Cotrina, Leyla Antoinette es_ES
renati.juror Paz Mayuri, Carlos Alberto es_ES
renati.juror Casas Chávez, Elizabeth Rosario es_ES


Files in this item

This item appears in the following Collection(s)

Show simple item record

info:eu-repo/semantics/openAccess Except where otherwise noted, this item's license is described as info:eu-repo/semantics/openAccess

Search DSpace


Browse

My Account

Statistics