Efectividad de pasta experimental a base de nanohidroxiapatita obtenida de la cáscara de huevo en la obliteración de túbulos dentinarios

Show simple item record

dc.contributor.advisor Tay Chu Jon, Lidia Yileng es_ES
dc.contributor.author Huaman Mujica, Karina es_ES
dc.date.accessioned 2022-10-26T18:01:09Z
dc.date.available 2022-10-26T18:01:09Z
dc.date.issued 2020
dc.identifier.other 102470 es_ES
dc.identifier.uri https://hdl.handle.net/20.500.12866/12487
dc.description.abstract En busca de un tratamiento eficaz, sostenible y económico para el manejo de la hipersensibilidad dentinaria (HD), el presente trabajo de investigación elaboró y evaluó el efecto de una pasta experimental a base de nanohidroxiapatita (nHAP) obtenida de la cáscara de huevo para la obliteración de los túbulos dentinarios (TDs), se sintetizó nHAP a partir de la cáscara de huevo. Se formularon pastas con diferentes porcentajes de esta nHAP: 3, 7 y 15%. Se utilizaron muestras de premolares y se dividieron en 5 grupos según la pasta aplicada: GI: 3% de nHAP, GII: 7% de nHAP, GIII: 15% de nHAP, GIV: pasta comercial con Zinc- Hidroxiapatita s/flúor (Biorepair®), grupo V: pasta sin nHAP. Las muestras fueron sometidas a un primer efecto erosivo con Coca Cola® durante 2 minutos. Luego se aplicaron las pastas y se cepillaron por 3 min c/24 horas durante 7 días. El segundo efecto erosivo fue en el día 15 de evaluación. Las muestras fueron analizadas mediante microscopía electrónica de barrido (MEB) y espectroscopia raman confocal (RAMAN) en tres momentos: después del primer ciclo erosivo, a los 7 días de las aplicaciones de las pastas y después del segundo efecto erosivo. El análisis cuantitativo de las muestras mostró una diferencia estadísticamente significativa entre los grupos (I, II, III) con respecto a los grupos (IV, V) (p<0,05) y ninguna diferencia estadísticamente significativa entre los grupos (I, II, III), el GI presentó una diferencia significativa con G5 (p<0,05) al evaluar la concentración de mineral a los 7 días. Se concluyó que la pasta experimental sintetizada a partir de la cáscara de huevo es efectiva en la obliteración de los TDs. es_ES
dc.description.abstract Searching for an effective, sustainable, and affordable treatment for the management of dental hypersensitivity (HD), this research created and evaluated the effects of an experimental nano-hydroxyapatite (nHAP) paste, obtained from eggshells, for the obliteration of the dentinal tubules (TDs). Nano-hydroxyapatite was synthesized from eggshells. Pastes with the following nHAP percentages were formulated: 3, 7 and 15%. Premolar teeth samples were utilized and divided into 5 groups according to the paste applied: GI: 3% nHAP, GII: 7% nHAP, GIII: 15% nHAP, GIV: commercial paste with Zinc-Hydroxyapatite s / fluorine (Biorepair®), group V: pasta without nHAP. The samples were subjected to an initial erosive-effect test with Coca Cola® for 2 minutes. Then, the pastes were applied to the samples and brushed for 3 minutes every 24 hours for 7 days. The second erosive-effect test was on day 15 of evaluation. The samples were analyzed through a scanning electron microscope (SEM) and confocal Raman spectroscopy (RAMAN) in three instances: after the first erosive cycle, 7 days after the application of the paste and after the second erosive-effect test. The quantitative analysis of the samples showed a statistically significant difference between the groups (I, II, III) in regards to the groups (IV, V) (p <0,05) and no statistically significant difference between the groups (I, II, III), the GI showed a significant difference with G5 (p <0,05) when evaluating the mineral concentration at 7 days. It was concluded that the experimental paste, synthesized from eggshells, is effective in obliterating the dentinal tubules. es_ES
dc.format application/pdf es_ES
dc.language.iso spa es_ES
dc.publisher Universidad Peruana Cayetano Heredia es_ES
dc.rights info:eu-repo/semantics/openAccess es_ES
dc.rights.uri https://creativecommons.org/licenses/by-nc-nd/4.0/deed.es es_ES
dc.subject Hidroxiapatita es_ES
dc.subject Pasta Dental es_ES
dc.subject Cascara de Huevo es_ES
dc.title Efectividad de pasta experimental a base de nanohidroxiapatita obtenida de la cáscara de huevo en la obliteración de túbulos dentinarios es_ES
dc.type info:eu-repo/semantics/doctoralThesis es_ES
thesis.degree.name Doctor en Estomatología es_ES
thesis.degree.grantor Universidad Peruana Cayetano Heredia. Escuela de Posgrado Víctor Alzamora Castro es_ES
thesis.degree.discipline Estomatología es_ES
dc.publisher.country PE es_ES
dc.subject.ocde http://purl.org/pe-repo/ocde/ford#2.07.05 es_ES
dc.subject.ocde http://purl.org/pe-repo/ocde/ford#3.02.14 es_ES
dc.subject.ocde http://purl.org/pe-repo/ocde/ford#4.02.01 es_ES
renati.author.dni 47157727
renati.advisor.orcid https://orcid.org/0000-0002-1656-2804 es_ES
renati.advisor.dni 41875787
renati.type http://purl.org/pe-repo/renati/type#tesis es_ES
renati.level http://purl.org/pe-repo/renati/nivel#doctor es_ES
renati.discipline 911018 es_ES
renati.juror Castillo Cevallos, Jorge Luis es_ES
renati.juror Beltrán Silva, Jorge Arturo es_ES
renati.juror Melgar Hermoza, Rosa Ana es_ES
renati.juror Díaz Pizán, María Elena es_ES


Files in this item

This item appears in the following Collection(s)

Show simple item record

info:eu-repo/semantics/openAccess Except where otherwise noted, this item's license is described as info:eu-repo/semantics/openAccess

Search DSpace


Browse

My Account

Statistics