Incorporación de nanohidroxiapatita obtenida de la cáscara de huevo en geles de peróxido de hidrógeno para la remineralización del esmalte durante el blanqueamiento

Roncal Espinoza, Rosa Josefina

dc.contributor.advisor	Tay Chu Jon, Lidia Yileng	es_ES
dc.contributor.author	Roncal Espinoza, Rosa Josefina	es_ES
dc.date.accessioned	2025-09-03T14:51:42Z
dc.date.available	2025-09-03T14:51:42Z
dc.date.issued	2025
dc.identifier.other	204931	es_ES
dc.identifier.uri	https://hdl.handle.net/20.500.12866/17601
dc.description.abstract	Objetivo: Evaluar los efectos de la incorporación de nanohidroxiapatita (nano-HA) obtenida de la cáscara de huevo en geles de peróxido de hidrógeno para la remineralización del esmalte durante el blanqueamiento. Material y métodos: se formularon geles a base de peróxido de hidrógeno (HP) al 10% y 35%, a los que se le incorporó diferentes concentraciones de hidroxiapatita (HA). Se asignaron de forma aleatoria 80 dientes de bovino en 8 grupos (n = 10): HP 10%, HP 10% + HA 3%, HP 10% + HA 6%, HP 35%, HP 35% + HA 3%, HP 35% + HA 6%, grupos control: Whiteness HP (FGM) y agua destilada. Se evaluó la cantidad relativa de mineral mediante espectroscopia Raman, los valores de microdureza se midieron con un microdurómetro Vickers. Todas las evaluaciones se realizaron antes y después de la exposición a los agentes blanqueadores (14 días), además de una semana posterior al blanqueamiento (21 días). Finalmente, se midió el color mediante un espectrofotómetro en cuatro tiempos. Resultados: Todos los grupos presentaron disminución de la cantidad relativa de mineral después de haber sido expuestos a los agentes blanqueadores; mientras que, una semana después del tratamiento, se observó una recuperación similar al agua en los grupos HP 10% y HP 10%+ HA 6% (p>0,05). Los valores de microdureza (MPa) no presentaron diferencias estadísticamente significativas. Todos los grupos experimentales generaron cambios de color en todos los tiempos. A los 7 días de tratamiento, el grupo HP 10%+HA 6% mostró un cambio de color mayor y con diferencias estadísticamente significativas. Conclusión: La incorporación de nanohidroxiapatita obtenida de la cáscara de huevo puede generar menos perdida relativa de mineral, no modifica la microdureza del esmalte y promueve mayor cambio de color durante el blanqueamiento.	es_ES
dc.description.abstract	Objective: To evaluate the effects of incorporating nanohydroxyapatite (nHA) obtained from eggshell into hydrogen peroxide gels for enamel remineralisation during bleaching. Materials and methods: 10% and 35% hydrogen peroxide (HP) based gels were formulated with different concentrations of hydroxyapatite (HA). Eighty bovine teeth were randomly assigned into eight groups (n = 10): HP 10%, HP 10% + HA 3%, HP 10% + HA 6%, HP 35%, HP 35% + HA 3%, HP 35% + HA 6%, control groups: whiteness HP (FGM) and distilled water. The relative amount of mineral was evaluated by Raman spectroscopy, microhardness values were measured with a Vickers microhardness tester. All evaluations were carried out before and after exposure to the bleaching agents (14 days), as well as one week after bleaching (21 days). Finally, colour was measured using a spectrophotometer at four times. Results: All groups showed a decrease in the relative amount of mineral after being exposed to the bleaching agents; whereas, one week after treatment, a similar recovery to water was observed in the HP 10% and HP10%+ HA 6% groups (p>0.05). The microhardness values (MPa) did not show statistically significant differences. All experimental groups generated colour changes at all times. At 7 days of treatment, the HP10%+ HA 6% groupshowed a greater colour change with statistically significant differences. Conclusion: The incorporation of nanohydroxyapatite obtained from eggshell can generate less relative mineral loss, does not modify enamel microhardness and promotes greater colour change during bleaching.	es_ES
dc.format	application/pdf	es_ES
dc.language.iso	spa	es_ES
dc.publisher	Universidad Peruana Cayetano Heredia	es_ES
dc.rights	info:eu-repo/semantics/openAccess	es_ES
dc.rights.uri	https://creativecommons.org/licenses/by-nc-nd/4.0/deed.es	es_ES
dc.subject	Hidroxiapatita	es_ES
dc.subject	Peróxido de hidrógeno	es_ES
dc.subject	Blanqueamiento	es_ES
dc.subject	Raman	es_ES
dc.subject	Microdureza	es_ES
dc.subject	Color	es_ES
dc.title	Incorporación de nanohidroxiapatita obtenida de la cáscara de huevo en geles de peróxido de hidrógeno para la remineralización del esmalte durante el blanqueamiento	es_ES
dc.type	info:eu-repo/semantics/doctoralThesis	es_ES
thesis.degree.name	Doctor en Estomatología	es_ES
thesis.degree.grantor	Universidad Peruana Cayetano Heredia. Escuela de Posgrado Víctor Alzamora Castro	es_ES
thesis.degree.discipline	Estomatología	es_ES
dc.publisher.country	PE	es_ES
dc.subject.ocde	https://purl.org/pe-repo/ocde/ford#3.02.14	es_ES
renati.author.dni	46707193
renati.advisor.orcid	https://orcid.org/0000-0002-1656-2804	es_ES
renati.advisor.dni	41875787
renati.type	https://purl.org/pe-repo/renati/type#tesis	es_ES
renati.level	https://purl.org/pe-repo/renati/level#doctor	es_ES
renati.discipline	911018	es_ES
renati.juror	Castillo Cevallos, Jorge Luis	es_ES
renati.juror	Mena Serrano, Alexandra Patricia	es_ES
renati.juror	Angeles Maslucan, Romy Janet	es_ES