Efecto de la temperatura ambiental y tiempo de espera posrefrigeración en la polimerización de una resina compuesta universal y una bulk fill

Melendez Murillo, Diego Alonso

dc.contributor.advisor	Delgado Cotrina, Leyla Antoinette	es_ES
dc.contributor.advisor	Tay Chu Jon, Lidia Yileng	es_ES
dc.contributor.author	Melendez Murillo, Diego Alonso	es_ES
dc.date.accessioned	2021-12-14T20:22:18Z
dc.date.available	2021-12-14T20:22:18Z
dc.date.issued	2021
dc.identifier.other	203334	es_ES
dc.identifier.uri	https://hdl.handle.net/20.500.12866/10315
dc.description.abstract	Antecedentes: La temperatura influye directamente en las propiedades mecánicas de una restauración, sobre todo en ambientes clínicos donde ésta se aleja de los 20°C o en el proceso de almacenamiento bajo refrigeración. Objetivo: Evaluar la influencia de la temperatura ambiental y el tiempo de espera posrefrigeración en la microdureza superficial de una resina compuesta universal y una bulk fill. Materiales y métodos: Se confeccionaron 105 discos de 5x5x4 mm de una resina compuesta bulk fill y discos de 5x5x2 mm de una resina universal y nanoparticulada. Para evaluar la temperatura de la resina, ésta se polimerizó a 4°C, 20°C y 30°C y para evaluar el tiempo de espera posrefrigeración se esperó 0, 10, 20 y 30 min antes de la fotoactivación. Luego de 24 h, se registró la microdureza de Vickers en las superficies superior e inferior de los discos. Los datos se analizaron mediante test descriptivos (media y desviación estándar) y test analíticos (ANOVA/Tukey) con un nivel de confianza del 0.5%. Resultados: Las diferentes temperaturas ambientales y los diferentes tiempos de espera posrefrigeración no presentaron diferencias estadísticamente significativas en los grupos de resina universal y bulk fill (p>0,05). Los valores de microdureza en todos los grupos presentaron una proporción de superficies inferior/superior mayor al 80%. Conclusión: La temperatura ambiental y el tiempo de espera posrefrigeración no influyeron en los valores de microdureza de la resina compuesta universal y bulk fill, sin embargo, una temperatura ambiental de 30ºC afectó positiviamente la microdureza de las resina compuesta nanoparticulada.	es_ES
dc.description.abstract	Background: The temperature has a direct influence on the mechanical properties of a restoration and is especially important in clinical settings where the environmental temperature drifts away from 20°C or in the refrigerated storage process. Objective: To evaluate the influence of environmental temperature and post-refrigeration bench time on the surface microhardness of a universal and a bulk-fill resin composite. Materials and methods: Discs of 5x5x4 mm of a bulkfill resin composite and discs of 5x5x2 mm of a universal and nanofilled resin composite were made. To evaluate the environmental temperature, the resin composite was cured at 4°C, 20°C and 30°C; and to evaluate the post-refrigeration bench time, 0, 10, 20 and 30 min were monitored before curing. After 24 h, the Vickers microhardness was recorded at the top and bottom surfaces of the discs. The data were analyzed by descriptive tests (mean and standard deviation) and analytical tests (ANOVA/Tukey) with a confidence level of 0.5%. Results: Different environmental temperatures and post-refrigeration bench times did not result in statistically different microhardness values in the universal and bulk-fill resin composite groups (p>0.05). Moreover, bottom surface microhardness values in all groups presented a >80% bottom/top ratio. Conclusions: Environmental temperature and bench time after refrigeration did not influence the microhardness values for the universal and bulk-fill resin composites, however, an environmental temperature of 30°C positively affected the microhardness of the nanofilled resin composites.	es_ES
dc.format	application/pdf	es_ES
dc.language.iso	spa	es_ES
dc.publisher	Universidad Peruana Cayetano Heredia	es_ES
dc.rights	info:eu-repo/semantics/openAccess	es_ES
dc.rights.uri	https://creativecommons.org/licenses/by-nc-nd/4.0/deed.es	es_ES
dc.subject	Resinas Compuestas	es_ES
dc.subject	Dureza	es_ES
dc.subject	Temperatura	es_ES
dc.subject	Refrigeración	es_ES
dc.title	Efecto de la temperatura ambiental y tiempo de espera posrefrigeración en la polimerización de una resina compuesta universal y una bulk fill	es_ES
dc.title.alternative	Effect of environmental temperature and postrefrigeration bench time on polymerization of a universal and a bulk-fill resin composite	es_ES
dc.type	info:eu-repo/semantics/monograph	es_ES
thesis.degree.name	Segunda Especial Profesional en Odontología Restauradora y Estética	es_ES
thesis.degree.grantor	Universidad Peruana Cayetano Heredia. Facultad de Estomatología Roberto Beltrán Neira	es_ES
thesis.degree.discipline	Odontología Restauradora y Estética	es_ES
dc.publisher.country	PE	es_ES
dc.subject.ocde	http://purl.org/pe-repo/ocde/ford#2.05.04	es_ES
dc.subject.ocde	http://purl.org/pe-repo/ocde/ford#3.02.14	es_ES
renati.author.dni	70112919
renati.advisor.orcid	https://orcid.org/0000-0002-3027-178X	es_ES
renati.advisor.orcid	https://orcid.org/0000-0002-1656-2804	es_ES
renati.advisor.dni	10193841
renati.advisor.dni	41875787
renati.type	http://purl.org/pe-repo/renati/type#tesis	es_ES
renati.level	http://purl.org/pe-repo/renati/nivel#tituloSegundaEspecialidad	es_ES
renati.discipline	911209	es_ES
renati.juror	Mas López, Janett	es_ES
renati.juror	Henostroza Quintans, Natalia	es_ES
renati.juror	Noborikawa Kohatsu, Andrés Kenichi	es_ES