Resistencia al cizallamiento de brackets cementados y fotopolimerizados con luz halógena y diodo emisor de luz a diferentes tiempos de exposición: estudio in vitro

Paipay Santos, Luis Gustavo

dc.contributor.advisor	Adriazola Pando, Lenin Manuel	es_ES
dc.contributor.author	Paipay Santos, Luis Gustavo	es_ES
dc.date.accessioned	2022-05-21T02:47:07Z
dc.date.available	2022-05-21T02:47:07Z
dc.date.issued	2021
dc.identifier.other	201580	es_ES
dc.identifier.uri	https://hdl.handle.net/20.500.12866/11664
dc.description.abstract	Antecedentes: Los sistemas de adhesión fotopolimerizables son utilizados ampliamente en ortodoncia. Por lo tanto, la eficacia de la polimerización con luz halógena o diodo emisor de luz (LED) es esencial para obtener un óptimo resultado. Objetivo: Comparar la resistencia a la fuerza de cizallamiento de los brackets cementados y fotopolimerizados con luz halógena y luz LED a diferentes tiempos de exposición. Material y métodos: Estudio in vitro. Los brackets fueron adheridos a 45 premolares humanos y divididos en tres grupos de acuerdo a la lámpara de polimerización y el tiempo de exposición utilizado: G1 (luz halógena, 40 segundos), G2 (LED, 10 segundos) y G3 (LED, 20 segundos). La muestra fue almacenada en agua destilada a temperatura ambiente y mantenidos en la oscuridad durante 24 horas, luego fueron sometidos a la prueba de resistencia a la fuerza de cizallamiento utilizando la máquina de ensayo universal. Resultados: La mayor resistencia a la fuerza de cizallamiento fue obtenido con luz halógena a 40 segundos (5,90 MPa ± 1,60) y la menor resistencia con luz LED a 10 segundos (4,02 MPa ± 1,49). De acuerdo al análisis de varianza ANOVA y la prueba post hoc de Tukey, se encontró que sólo el grupo G1 presentó diferencia estadísticamente significativa (p<0,05). Conclusión: Los brackets fotopolimerizados con luz halógena a 40 segundos mostraron la mayor resistencia a la fuerza de cizallamiento.	es_ES
dc.description.abstract	Background: Light-curing bonding systems are widely used in orthodontics. Therefore, the efficiency of halogen or light-emitting diode (LED) polymerization is essential for optimal results. Objective: Compare the resistance to the shear force of cemented and light-cured brackets with halogen light and LED light at different exposure times. Material and methods: In vitro study. Brackets were bonded to 45 human premolars and divided into three groups according to the curing light and the exposure time used: G1 (halogen light, 40 seconds), G2 (LED, 10 seconds), and G3 (LED, 20 seconds). The sample was stored in distilled water at room temperature and kept in darkness for 24 hours, then they were subjected to the test of resistance to shear force using the universal testing machine. Results: The highest resistance to shear force was obtained with halogen light at 40 seconds (5.90 MPa ± 1.60) and the lowest with LED light at 10 seconds (4.02 MPa ± 1.49). According to the analysis of variance ANOVA and Tukey's post hoc test, it was found that only the G1 group presented a statistically significant difference (p <0.05). Conclusion: Brackets light-cured with halogen light at 40 seconds showed the highest resistance to shear force.	es_ES
dc.format	application/pdf	es_ES
dc.language.iso	spa	es_ES
dc.publisher	Universidad Peruana Cayetano Heredia	es_ES
dc.rights	info:eu-repo/semantics/openAccess	es_ES
dc.rights.uri	https://creativecommons.org/licenses/by-nc-nd/4.0/deed.es	es_ES
dc.subject	Resistencia al Corte	es_ES
dc.subject	Polimerización	es_ES
dc.subject	Luces de Curación	es_ES
dc.title	Resistencia al cizallamiento de brackets cementados y fotopolimerizados con luz halógena y diodo emisor de luz a diferentes tiempos de exposición: estudio in vitro	es_ES
dc.title.alternative	Shear bond strength of orthodontic brackets bonded and photopolimerized through halogen light and light-emitting diode at different times of exposure: in vitro study	es_ES
dc.type	info:eu-repo/semantics/monograph	es_ES
thesis.degree.name	Especialista en Ortodoncia y Ortopedia Maxilar	es_ES
thesis.degree.grantor	Universidad Peruana Cayetano Heredia. Facultad de Estomatología Roberto Beltrán Neira	es_ES
thesis.degree.discipline	Ortodoncia y Ortopedia Maxilar	es_ES
dc.publisher.country	PE	es_ES
dc.subject.ocde	http://purl.org/pe-repo/ocde/ford#3.02.14	es_ES
renati.author.dni	46419847
renati.advisor.orcid	https://orcid.org/0000-0002-4739-1155	es_ES
renati.advisor.dni	06177177
renati.type	http://purl.org/pe-repo/renati/type#tesis	es_ES
renati.level	http://purl.org/pe-repo/renati/nivel#tituloSegundaEspecialidad	es_ES
renati.discipline	911269	es_ES
renati.juror	Tuesta Da Cruz, Orlando	es_ES
renati.juror	Vidalón Castilla, José Antonio	es_ES
renati.juror	Melgar Gutiérrez, Jorge Carlos	es_ES