Resistencia a las fuerzas de cizallamiento de tres agentes cementantes sobre brackets metálicos, en superficies de resina acrílica de termocurado arenadas y fresadas. In vitro

Ponce Arias, Evelyn Gazdally

dc.contributor.advisor	Quiñe Angeles, Aldo Rafael	es_ES
dc.contributor.author	Ponce Arias, Evelyn Gazdally	es_ES
dc.date.accessioned	2024-08-08T20:06:06Z
dc.date.available	2024-08-08T20:06:06Z
dc.date.issued	2024
dc.identifier.other	100685	es_ES
dc.identifier.uri	https://hdl.handle.net/20.500.12866/15725
dc.description.abstract	Introducción: La resistencia al cizallamiento permite medir la fuerza necesaria entre la unión de dos materiales al aplicar fuerzas paralelas de sentido contrario.Objetivo: Comparar la resistencia a las fuerzas de cizallamiento de tres agentes cementantes sobre brackets metálicos, en superficies de resina acrílica de termocurado, arenadas y fresadas. Materiales y métodos: 120 bloques de resina acrílica de termocurado, fueron divididas en 6 grupos (20 superficies cada grupo). Tres grupos fueron adheridos con tres agentes cementantes a superficies arenadas, y los otros tres grupos fueron adheridos con tres agentes cementantes a superficies fresadas, utilizando brackets metálicos EDGEWISE slot 0.022’’ (American Orthodontics 3524 Washington Ave, Sheboygan, WI 53081, EE. UU), resina acrílica Duralay, resina Orthocem y resina TransbondTM XT. Resultados: El valor máximo fue del grupo fresado con Duralay (6,52 MPa ± 1,45) y valor mínimo se encontró en el Orthocem (2,68 MPa ± 0,74), en superficies fresadas. La resina fotopolimerizable Orthocem tuvo una media de fuerza de cizallamiento de 6.39 (DS ±1.32), la resina acrílica Duralay obtuvo una media de 4.20 (DS±1.30) y la resina fotopolimerizable TransbondTM XTuna media de 6.39 (DS±1.27) en superficies arenadas. En cuanto a las superficies fresadas la resina fotopolimerizable Orthocem tuvo una fuerza de cizallamiento de 2.68 (DS ±0.74), la resina acrílica Duralay una media de 6.52 (DS±1.45) y la resina fotopolimerizable TransbondTM XT una media de 4.28 (DS±1.33) en superficies arenadas. Conclusión: Si hubo diferencias significativas en todos los grupos según tipo de tratamiento de superficie al usar la misma resina.	es_ES
dc.description.abstract	Introduction: Shear resistance allows measuringthe force necessary between the union of two materials when applying parallel forces in opposite directions . Aim: Compare the resistance to shear forces of three cementing agents on metal brackets, on thermocured acrylic resin surfaces, sandblasted and milled. Materials and methods: 120 blocks of thermocuring acrylic resin were divided into 6 groups (20 surfaces each group). Three groups were bonded with three cementing agents to sandblasted surfaces, and the other three groups were bonded with three cementing agents to milled surfaces, using EDGEWISE slot 0.022'' metal brackets (American Orthodontics 3524 Washington Ave, Sheboygan, WI 53081, USA), Duralay acrylic resin, Orthocem resin and TransbondTM XT resin. Results: The maximum value was in the group milled with Duralay (6.52 MPa ± 1.45) and the minimum value was found in the Orthocem (2.68 MPa ± 0.74), in milled surfaces. The Orthocem photopolymerizable resin had an average shear strength of 6.39 (DS ±1.32), the Duralay acrylic resin obtained an average of 4.20 (DS±1.30) and TransbondTM XT photopolymerizable resin an average of 6.39 (DS±1.27) on sandblasted surfaces. Regarding the milled surfaces, the Orthocem photopolymerizable resin had shear force of 2.68 (DS ±0.74), the Duralay acrylic resin an average of 6.52 (DS±1.45) and TransbondTM XT photopolymerizable resin a mean of 4.28 (DS±1.33) on sandblasted surfaces. Conclusion: There were significant differences in all groups depending on the type of surface treatment when using the same resin.	es_ES
dc.format	application/pdf	es_ES
dc.language.iso	spa	es_ES
dc.publisher	Universidad Peruana Cayetano Heredia	es_ES
dc.rights	info:eu-repo/semantics/openAccess	es_ES
dc.rights.uri	https://creativecommons.org/licenses/by-nc-nd/4.0/deed.es	es_ES
dc.subject	Resistencia al Corte	es_ES
dc.subject	Soportes Ortodóncicos	es_ES
dc.subject	Resinas Compuestas	es_ES
dc.subject	Resinas Acrílicas	es_ES
dc.subject	Aparato Fijo de Ortodoncia	es_ES
dc.title	Resistencia a las fuerzas de cizallamiento de tres agentes cementantes sobre brackets metálicos, en superficies de resina acrílica de termocurado arenadas y fresadas. In vitro	es_ES
dc.title.alternative	Resistance to the shear forces of three cementing agents on metal brackets, in sandblasted and milled thermocured acrylic resin superfaces. in vitro	es_ES
dc.type	info:eu-repo/semantics/monograph	es_ES
thesis.degree.name	Especialista en Ortodoncia y Ortopedia Maxilar	es_ES
thesis.degree.grantor	Universidad Peruana Cayetano Heredia. Facultad de Estomatología Roberto Beltrán Neira	es_ES
thesis.degree.discipline	Ortodoncia y Ortopedia Maxilar	es_ES
dc.publisher.country	PE	es_ES
dc.subject.ocde	http://purl.org/pe-repo/ocde/ford#2.05.02	es_ES
dc.subject.ocde	http://purl.org/pe-repo/ocde/ford#3.02.14	es_ES
renati.author.dni	44691777
renati.advisor.orcid	https://orcid.org/0009-0008-7030-804X	es_ES
renati.advisor.dni	10881316
renati.type	https://purl.org/pe-repo/renati/type#tesis	es_ES
renati.level	https://purl.org/pe-repo/renati/level#tituloSegundaEspecialidad	es_ES
renati.discipline	911269	es_ES
renati.juror	Tuesta Da Cruz, Orlando	es_ES
renati.juror	Liñan Duran, Carlos Yuri	es_ES
renati.juror	Melgar Gutierrez, Jorge Carlos	es_ES