Resistencia adhesiva en diferentes protocolos de tratamiento de superficie usando bloques de cerámica de matriz de resina para CAD/CAM

Mostrar el registro sencillo del ítem

dc.contributor.advisor Balarezo Razzeto, Jose Antonio es_ES
dc.contributor.author Saravia Rojas, Miguel Angel es_ES
dc.contributor.author Huanambal Tiravanti, Victor Abel es_ES
dc.date.accessioned 2024-09-20T14:58:00Z
dc.date.available 2024-09-20T14:58:00Z
dc.date.issued 2024
dc.identifier.other 208038 es_ES
dc.identifier.uri https://hdl.handle.net/20.500.12866/16107
dc.description.abstract Antecedentes: La diversa composición química de las cerámicas híbridas (HC) CAD/CAM introducidas recientemente ha dado lugar a hallazgos contradictorios sobre el impacto de los tratamientos superficiales antes de la cementación, lo que complica el establecimiento de un protocolo clínico universalmente aceptado. Objetivo: Evaluar la influencia de diferentes tratamientos superficiales de cerámicas híbridas, sobre la fuerza de adhesión de un cemento resinoso. Material y métodos. Se utilizaron seis tipos de cerámicas modificadas, que fueron sometidas a cuatro tratamientos de superficie diferentes: sin tratamiento (control), abrasión con partículas de Al2O3, acondicionamiento con HF al 9%, y una combinación de Al2O3 y HF. Tras los tratamientos, se aplicó un agente de acoplamiento de silano y se colocaron cilindros de cemento de resina en las muestras, los cuales se polimerizaron y se sometieron a pruebas de microshear para medir la fuerza de adhesión. Resultados: Después de 24 horas, todos los tratamientos mejoraron significativamente la fuerza de adhesión en comparación con el control en la cerámica Evolux. La combinación de Al2O3 y HF generó la mayor fuerza de adhesión en varias cerámicas, excepto en Alium, donde la abrasión con Al2O3 fue más efectiva. Después del ciclo térmico, todos los tratamientos mostraron una mejora en la adhesión en comparación con el control. Sin embargo, el HF tuvo un efecto negativo en la cerámica Vita Enamic, alterando significativamente su superficie y reduciendo la fuerza de adhesión. En términos de composición, Vita Enamic fue la única cerámica que presentó tanto compuestos orgánicos como inorgánicos, mientras que las demás cerámicas mostraron una composición predominantemente orgánica. Conclusion: La abrasión con Al2O3 seguida de HF resultó ser el tratamiento más efectivo para la mayoría de las cerámicas, destacando la importancia de seleccionar el tratamiento de superficie adecuado para optimizar la adhesión en cerámicas modificadas con resina. es_ES
dc.description.abstract Background: The diverse chemical composition of recently introduced resin-modified ceramics complicates the establishment of a universally accepted clinical bonding protocol. Objective: Evaluate the influence of different surface treatments of resin-modified ceramics on the bond strength to a resin cement. Methods and Materials. Six types of resin-modified ceramics were used, with samples divided into four groups based on surface treatments: no treatment (control), airborne-particle abrasion with Al2O3, conditioning with 9% HF, and a combination of Al2O3 and HF. After applying these treatments, a silane coupling agent was used, and resin cement cylinders were bonded to the samples, which were then light-cured. The bond strength was tested through microshear after 24 hours, with half of the samples also undergoing thermocycling. Results: All surface treatments significantly improved bond strength compared to the control group, particularly in the Evolux ceramic. The combination of Al2O3 and HF provided the highest bond strength in most ceramics, except for Alium, where Al2O3 alone was more effective. Post-thermocycling results showed that all treatments increased bond strength relative to the control, but HF treatment negatively impacted the Vita Enamic ceramic, causing notable surface alterations that reduced bond strength. Adhesive failures were prevalent in untreated samples, whereas mixed failures were common after surface treatments. The study also observed that Al2O3 treatment altered the surface of all resin-modified ceramics, with HF notably affecting Vita Enamic. The combined Al2O3 and HF treatment significantly modified Vita Enamic and the other ceramics. Vita Enamic was unique in displaying both organic and inorganic compositions, while the other ceramics were predominantly organic. Conclusion: airborne-particle abrasion with Al2O3 followed by HF yielded the highest bond strength across most resin-modified ceramics, except for Alium. The findings highlight the importance of selecting appropriate surface treatments to optimize bond strength in resin-modified ceramics. es_ES
dc.format application/pdf es_ES
dc.language.iso spa es_ES
dc.publisher Universidad Peruana Cayetano Heredia es_ES
dc.rights info:eu-repo/semantics/openAccess es_ES
dc.rights.uri https://creativecommons.org/licenses/by-nc-nd/4.0/deed.es es_ES
dc.subject Cerámica Híbrida CAD/CAM es_ES
dc.subject Tratamiento Superficial es_ES
dc.subject Resistencia de Unión por Microcizallamiento es_ES
dc.subject Cemento de Resina es_ES
dc.subject Termociclado es_ES
dc.title Resistencia adhesiva en diferentes protocolos de tratamiento de superficie usando bloques de cerámica de matriz de resina para CAD/CAM es_ES
dc.title.alternative Adhesive strength using different surface treatment protocols using resin matrix ceramic blocks for CAD/CAM es_ES
dc.type info:eu-repo/semantics/monograph es_ES
thesis.degree.name Especialista en Odontología Restauradora y Estética es_ES
thesis.degree.grantor Universidad Peruana Cayetano Heredia. Facultad de Estomatología Roberto Beltrán Neira es_ES
thesis.degree.discipline Odontología Restauradora y Estética es_ES
dc.publisher.country PE es_ES
dc.subject.ocde http://purl.org/pe-repo/ocde/ford#2.05.02 es_ES
dc.subject.ocde http://purl.org/pe-repo/ocde/ford#3.02.14 es_ES
renati.author.dni 06109026
renati.author.dni 10550012
renati.advisor.orcid https://orcid.org/0000-0003-1794-4908 es_ES
renati.advisor.dni 06300461
renati.type https://purl.org/pe-repo/renati/type#tesis es_ES
renati.level https://purl.org/pe-repo/renati/level#tituloSegundaEspecialidad es_ES
renati.discipline 911209 es_ES
renati.juror Mendiola Aquino, Carlos Enrique es_ES
renati.juror Avalos Dianderas, Cesar Augusto es_ES
renati.juror Maldonado Mendoza, Maria de las Mercedes es_ES


Ficheros en el ítem

Este ítem aparece en la(s) siguiente(s) colección(ones)

Mostrar el registro sencillo del ítem

info:eu-repo/semantics/openAccess Excepto si se señala otra cosa, la licencia del ítem se describe como info:eu-repo/semantics/openAccess

Buscar en el Repositorio


Listar

Panel de Control

Estadísticas