“Evaluación de una pasta dental experimental a base de quitosano y nano hidroxiapatita para la remineralización del esmalte dental. Estudio in vitro”

Huanambal Tiravanti, Victor Abel

dc.contributor.advisor	Tay Chu Jon, Lidia Yileng	es_ES
dc.contributor.author	Huanambal Tiravanti, Victor Abel	es_ES
dc.date.accessioned	2025-03-10T13:41:37Z
dc.date.available	2025-03-10T13:41:37Z
dc.date.issued	2024
dc.identifier.other	202118	es_ES
dc.identifier.uri	https://hdl.handle.net/20.500.12866/16830
dc.description.abstract	El objetivo del presente estudio fue evaluar el efecto remineralizante de una pasta dental experimental a base de nanohidroxiapatita y quitosano (nHAP/Q), como alternativa para favorecer la remineralización del esmalte dental bovino erosionado. Se evaluó el grado de mineralización mediante microscopia RAMAN y la microdureza superficial con Vickers. Se formuló una pasta dental base (PDB) que actuó como vehículo para los agentes remineralizantes en experimentación. Se elaboraron las siguientes pastas experimentales: PDB 80% + nHAp 10% + Quitosano 10%. (Grupo 1), PDB 90.%+ nHAp Concha de Abanico 10% (Grupo 2), PDB 90% + Quitosano 10%. (Grupo 3), PDB 90%+ nHAp comercial 10% (Grupo 4). Se establecieron como controles positivos 2 pastas dentales comerciales fluoradas de demostrada actividad remineralizante: Colgate total (Grupo 5) y Mi paste plus (Grupo 6). Se establecieron además los siguientes controles: PDB 100% (Grupo 7), Control ciclo erosivo, no pastas, conservación en saliva artificial (Grupo 8), Control no ciclo erosivo, no pastas (Grupo 9), Control ciclo erosivo, no pastas, conservación agua destilada (Grupo 10). Se establecieron 10 grupos de estudio con 10 muestras de esmalte de bovino cada uno, todos los especímenes de los grupos excepto del grupo 9 recibieron ataques con ácido cítrico al 0.5 % durante 2 min a las 0, 8, 24 y 32 horas. Después de cada ataque ácido, se aplicó las pastas de dientes correspondientes a cada grupo de tratamiento, excepto los grupos control 8, 9 y 10. Luego se procedió a evaluar el grado de mineralización mediante microscopia RAMAN y la microdureza superficial con Vickers. No encontramos diferencias significativas (p>0.05) en el grado de mineralización y Dureza superficial en el esmalte dental bovino, entre las diferentes pastas, las muestras de esmalte sano grupo 9) a las que no se les realizó ataque acido ni ningún tratamiento, ni las muestras del grupo 8 que recibieron el ataque ácido y fueron conservadas en saliva artificial. Pero si todas ellas, tienen diferencias significativas (p< 0.05) con el grupo 10 que fue sometido a ciclo erosivo y conservado en agua destilada. Este estudio in vitro muestra que la pasta experimental a base de nanohidroxiapatita y quitosano, tiene potencial remineralizante en el esmalte bovino erosionado.	es_ES
dc.description.abstract	The objective of the present study was to evaluate the remineralizing effect of AN experimental toothpaste based on nanohydroxyapatite and chitosan (nHAP/Q), as an alternative to promote the remineralization of eroded bovine tooth enamel. The degree of mineralization was evaluated using RAMAN microscopy and the surface microhardness with Vickers. A base toothpaste (PDB) was formulated that acted as a vehicle for the remineralizing agents under experimentation. The following experimental pastes were prepared: PDB 80% + nHAp 10% + Chitosan 10% (Group 1), PDB 90%+ nHAp Argopten purpuratus Shell 10% (Group 2), PDB 90% + Chitosan 10% (Group 3), PDB 90%+ commercial nHAp 10% (Group 4). Two fluorinated commercial toothpastes with proven remineralizing activity were established as positive controls: Colgate total® (Group 5) and MI Paste PlusTM (Group 6). The following controls were also established: PDB 100% (Group 7), erosive cycle control, without pastes, and conserved in artificial saliva (Group 8), non-erosive cycle control, without pastes (Group 9), erosive cycle control, without pastes, conserved in distilled water (Group 10). 10 study groups were established with 10 bovine enamel samples each, all the specimens of all the groups except Group 9 received attacks with 0.5% citric acid for 2 min at 0, 8, 24 and 32 hours. After each acid attack, the toothpastes corresponding to each treatment group were applied, except for control groups 8, 9 and 10. The degree of mineralization was then evaluated using RAMAN microscopy and surface microhardness with Vickers. No significant differences (p>0.05) were found in the intensity of the phosphate ion using Raman v1, nor in the Vickers Hardness (kg/mm2) of bovine enamel, between the different pastes, the healthy enamel samples (group 9) towhich no acid attack or any treatment was carried out, nor the samples from group 8 that received the acid attack and were preserved in artificial saliva. But all of them have significant differences (p < 0.05) with group 10 that was subjected to an erosive cycle and preserved in distilled water. This in vitro study shows that, the experimental pastes based on nanohydroxyapatite and chitosan, has a potential remineralizing effect on eroded bovine tooth enamel.	es_ES
dc.format	application/pdf	es_ES
dc.language.iso	spa	es_ES
dc.publisher	Universidad Peruana Cayetano Heredia	es_ES
dc.rights	info:eu-repo/semantics/openAccess	es_ES
dc.rights.uri	https://creativecommons.org/licenses/by-nc-nd/4.0/deed.es	es_ES
dc.subject	Hidroxiapatita	es_ES
dc.subject	Pastas de Dientes	es_ES
dc.subject	Quitosano	es_ES
dc.subject	Remineralización Dental	es_ES
dc.subject	Esmalte Dental	es_ES
dc.subject	Erosión de los Dientes	es_ES
dc.title	“Evaluación de una pasta dental experimental a base de quitosano y nano hidroxiapatita para la remineralización del esmalte dental. Estudio in vitro”	es_ES
dc.type	info:eu-repo/semantics/doctoralThesis	es_ES
thesis.degree.name	Doctor en Estomatología	es_ES
thesis.degree.grantor	Universidad Peruana Cayetano Heredia. Escuela de Posgrado Víctor Alzamora Castro	es_ES
thesis.degree.discipline	Estomatología	es_ES
dc.publisher.country	PE	es_ES
dc.subject.ocde	http://purl.org/pe-repo/ocde/ford#1.06.03	es_ES
dc.subject.ocde	http://purl.org/pe-repo/ocde/ford#3.02.14	es_ES
renati.author.dni	10550012
renati.advisor.orcid	https://orcid.org/0000-0002-1656-2804	es_ES
renati.advisor.dni	41875787
renati.type	https://purl.org/pe-repo/renati/type#tesis	es_ES
renati.level	https://purl.org/pe-repo/renati/level#doctor	es_ES
renati.discipline	911018	es_ES
renati.juror	Mena Serrano, Alexandra	es_ES
renati.juror	Bueno, Tamires	es_ES
renati.juror	Castillo Andamayo, Diana	es_ES